![]() ![]() Netsol Water products and solutions can provide the water your plant requires at every stage! Professionals in the water quality business can provide more extensive assistance and specialized recommendations when it comes to selecting the proper water treatment for residential or industrial water softening. ![]() With a larger degree of cross-linking, such as macroporous resin, the structure is robust and can sustain repeated regeneration. In general, resins with a low degree of cross-linking are more readily broken, but the uniformity and strength of the cross-linked structure dictate the resin's longevity. (5) Durabilityĭuring usage, the resin particles undergo changes such as transfer, friction, expansion and contraction, and there will be some loss and fracture over a long period of time, therefore the resin must have a greater mechanical strength and wear resistance. The swelling degree of the resin must be addressed while constructing the ion exchange device in order to adjust to the resin volume change produced by ion conversion in the resin during manufacturing. When the ions in the resin change, such as the cationic resin changing from H+ to Na+ and the anionic resin changing from Cl- to OH-, both expand owing to the increase in ion diameter, increasing the resin volume.Ī resin with a low degree of crosslinking has a higher degree of expansion in general. When ion exchange resin comes into touch with water, it has a significant number of hydrophilic groups, which cause it to expand. Resins with more active groups and less cross-linking have a higher tendency to disintegrate. The compounds incorporated in the resin synthesis process with a low degree of polymerization, as well as the substances created by the degradation of the resin, will dissolve away during operation. It's best if the ion exchange resin is insoluble. The real density of styrene-based gel-type strong acid cation resin is 1.26g/mL, while the apparent density is 0.85g/mL the true density of acrylic gel-type weak acid cation resin is 1.19g/mL, while the apparent density is 0.75g/mL. A resin with a high degree of crosslinking has a higher density than a weak acid or weak basic resin, while a macroporous resin has a lower density than a resin with a weak acid or weak basic resin. The degree of crosslinking and the type of the exchange group determine the resin's density. The apparent density is defined as the weight of wet resin per unit volume (including the spacing between particles). True density refers to the density of the resin when it is completely dry. On the coordinate chart of the "effective particle size" of the resin, it is the ratio of the corresponding sieve hole diameter to the effective particle size by taking the cumulative retained quantity of 40% particles. The homogeneity coefficient indicates whether the resin particles are homogeneous. Most popular resin products have effective particle sizes of 0.4 to 0.6 mm. The "effective particle size" of the resin is measured by the mesh diameter. The resin is sieved once it has entirely absorbed and swollen, and the residual quantity is gathered on the 20, 30, 40, 50mesh screen, through which 90 percent of the particles can pass. Wet sieving is commonly used to determine the size of resin particles. If the resin particle size is less than 0.2mm (about 70 mesh), it will greatly increase the fluid's resistance to pass, lowering the flow rate. As a result, the resin particle size should be correctly chosen. The resin particles are finer, the reaction speed is faster, but the fine particles' resistance to the passage of the liquid is greater, necessitating a higher working pressure this effect is amplified by the concentrated sugar liquid's high viscosity. Ion exchange resins are often formed into little beads, and the size of the beads is also significant. Ion exchange resin's particle size and associated physical parameters have a significant impact on its work and performance. What are the physical properties of Ion exchange resins?
0 Comments
Leave a Reply. |
AuthorWrite something about yourself. No need to be fancy, just an overview. ArchivesCategories |